RESUMEN
In this study, we investigated the impact of benzophenone (BP), a small molecule additive, on the performance and stability of inverted perovskite solar cells (PSCs). Specifically, we introduced BP into the perovskite precursor solution of FAPbI3 to fabricate PSCs with an ITO/PEDOT:PSS/BP:FAPbI3/PCBM/C60/PCB/Ag architecture. The incorporation of BP with an optimum concentration of 2 mg mL-1 significantly enhanced the power conversion efficiency (PCE) of the inverted PSC from 13.12 to 18.84% with negligible hysteresis. Notably, the BP-based PSCs retained â¼90% of their initial PCE after being stored in ambient air with 30% relative humidity at 25 °C for 700 h. In contrast, control devices showed rapid degradation, retaining only 30% of their initial value within 300 h under the same conditions. We attributed the superior performance and stability of the BP-based PSCs to the grain boundary passivation of the perovskite film. The improvement was mainly attributed to the intermolecular interaction between the O-donor Lewis base BP material and both Pb2+ and FA+ in FAPbI3. This effectively suppresses trap-assisted recombination and promotes the conversion of the δ-phase to photoactive and stable α-phase FAPbI3. Overall, our findings suggest that BP is a promising additive for improving the performance and stability of inverted PSCs.
RESUMEN
It has been a challenge to use transition metal oxides as anode materials in Li-ion batteries due to their low electronic conductivity, poor rate capability and large volume change during charge/discharge processes. Here, we present the first demonstration of a unique self-recovery of capacity in transition metal oxide anodes. This was achieved by reducing tungsten trioxide (WO3) via the incorporation of urea, followed by annealing in a nitrogen environment. The reduced WO3 successfully self-retained the Li-ion cell capacity after undergoing a sharp decrease upon cycling. Significantly, the reduced WO3 also exhibited excellent rate capability. The reduced WO3 exhibited an interesting cycling phenomenon where the capacity was significantly self-recovered after an initial sharp decrease. The quick self-recoveries of 193.21%, 179.19% and 166.38% for the reduced WO3 were observed at the 15th (521.59/457.41 mA h g-1), 36th (538.49/536.61 mA h g-1) and 45th (555.39/555.39 mA h g-1) cycles respectively compared to their respective preceding discharge capacity. This unique self-recovery phenomenon can be attributed to the lithium plating and conversion reaction which might be due to the activation of oxygen vacancies that act as defects which make the WO3 electrode more electrochemically reactive with cycling. The reduced WO3 exhibited a superior electrochemical performance with 959.1/638.9 mA h g-1 (1st cycle) and 558.68/550.23 mA h g-1 (100th cycle) vs. pristine WO3 with 670.16/403.79 mA h g-1 (1st cycle) and 236.53/234.39 mA h g-1 (100th cycle) at a current density of 100 mA g-1.
RESUMEN
Solution processed poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) transparent electrodes (TEs) offer great potential as a low cost alternative to expensive indium tin oxide (ITO). However, strong acids are typically used for enhancing the conductivity of PEDOT:PSS TEs, which produce processing complexity and environmental issues. This work presents an environmentally friendly acid free approach to enhance the conductivity of PEDOT:PSS using a light oxygen plasma treatment, in addition to solvent blend additives and post treatments. The plasma treatment was found to significantly reduce the sheet resistance of PEDOT:PSS TEs from 85 to as low as 15 Ω sq-1, which translates to the highest reported conductivity of 5012 S/cm for PEDOT:PSS TEs. The plasma treated PEDOT:PSS TE resulted in an ITO-free perovskite solar cell efficiency of 10.5%, which is the highest reported efficiency for ITO-free perovskite solar cells with a PEDOT:PSS electrode that excludes the use of acid treatments. This research presents the first demonstration of this technology. Moreover, the PEDOT:PSS TEs enabled better charge extraction from the perovskite solar cells and reduced hysteresis in the current density-voltage (J-V) curves.
RESUMEN
A hierarchical mesoporous carbon foam (ECF) with an interconnected micro-/mesoporous architecture was prepared and used as a binder-free, low-cost, high-performance anode for lithium ion batteries. Due to its high specific surface area (980.6 m2/g), high porosity (99.6%), light weight (5 mg/cm3) and narrow pore size distribution (~2 to 5 nm), the ECF anode exhibited a high reversible specific capacity of 455 mAh/g. Experimental results also demonstrated that the anode thickness significantly influence the specific capacity of the battery. Meanwhile, the ECF anode retained a high rate performance and an excellent cycling performance approaching 100% of its initial capacity over 300 cycles at 0.1 A/g. In addition, no binders, carbon additives or current collectors are added to the ECF based cells that will increase the total weight of devices. The high electrochemical performance was mainly attributed to the combined favorable hierarchical structures which can facilitate the Li+ accessibility and also enable the fast diffusion of electron into the electrode during the charge and discharge process. The synthesis process used to make this elastic carbon foam is readily scalable to industrial applications in energy storage devices such as li-ion battery and supercapacitor.
